ESTIMATION OF THE POROSITY OF PORTLAND CEMENT PASTES USING BACKSCATTERED ELECTRON IMAGE
Résumé
Microscopy plays an important role in the examination of cementitious materials. Electron-optical techniques allow
examination of microstructural details. The increased application of scanning electron microscopy in cement and concrete
investigations has brought attention to the estimation of the porosity. Backscattered Electron image has been established as a
method for quantitative analysis of hardened cement paste. This paper describes work and its application to Ordinary Portland
cement paste. Results show that the technique can be used to determine the porosity of Portland cement pastes. The success of
these investigations is, influenced by the type and quality of specimen preparation. In particular, backscattered electron and Xray
imaging modes are influenced by the specimen surface characteristics, with the ideal surface being highly polished. The
technique can be a powerful tool to determine this essential factor of durability in concrete materials.
Keys words: porosities, cement paste, strength, Scanning electron microscope, methanol exchange.
Références
and Computer Modelling of Hydration of Portland
Cement Particles. Petrography of Cementitious
Materials, ASTM STP 1215, Sharon M. DeHayes and
David Stark, Eds., American Society for Testing and
Materials, Philadelphia, pp. 60-73, 1994
2. Hall M G ; The application and programming of an
image store for the Scanning Electron Microscope;
Scanning, vol 13 N° 3, 1991
3. Mellas et al; Estimations of degree of hydration of
Portland cement pastes. Cement and Concrete
Research, vol 23, pp 399-405, 1993
4. Orr C.: Application of mercury penetration to material
analysis. Powder Technology, vol 3, 1970.
5. Parrott , L. J., “Effect of drying history upon the
exchange of pore water with methanol and upon
subsequent methanol sorption behaviour in hydrated
alite paste”, Cement and Concrete Research, Vol 11,
1981, p 651 – 658.
6. Scrivener, K L and Pratt, P L; Backscattered
Electron Images of Polished Cement Section in the
Scanning Electron Microscope. Proc. 6th int. Conf. On
Cement Microscopy, 26 – 29,March 1984,
Albubkerque , New Mexico, pp 145 – 155.
7. Shi D. and Winslow D N. : Contact angle and damage
during mercury intrusion into cement paste. Cement
and Concrete Research, vol 15, 1985
8. Stutzman P E & Clifton J R; Specimen preparation
for Scanning Electron Microscopy. Proceedings of the
twenty-First international conference on cement
microscopy. April 25-29,1999, Las vegas, Nevada, pp
10-22,1999